Investigate the Microstructure and the Mechanical Properties of Ni-Ti-Cu Shape Memory Alloys
Keywords:
shape memory alloys, powder metallurgy, porosity, compression strength, shape memory effectAbstract
Abstract
In this study a Nickel-Titanium-Cupper shape memory alloys was manufactured by powder metallurgy (PM) technique, powder mixture of 50% Ti , 47% Ni and 3% Cu was prepared by mixing for two hours and compacted in a press machine using various compacting pressure (600, 700 and 800) MPa , sample was then sintered for 5 hrs in an electrical tube vacuum furnace using sintering temperature of (850?C, 900?C and 950?C) .phase analysis of samples was conducted by X-ray diffraction test, the effect of different sintering temperature and compacting pressure on the porosity, microhardness ,compression strength and the shape memory effect (SME) was studied, the result showed decrease in the porosity and increasing in the shape recovery ,compression strength and microhardness with increasing compacting pressure and at lower sintering temperature and hence the best results was at 800MPa compacting pressure and 850?C sintering temperature.
Downloads
Downloads
Published
Issue
Section
License
The authors retain the copyright of their manuscript by submitting the work to this journal, and all open access articles are distributed under the terms of the Creative Commons Attribution-NonCommercial 4.0 International (CC-BY-NC 4.0), which permits use for any non-commercial purpose, distribution, and reproduction in any medium, provided that the original work is properly cited.