Go to Editorial ManagerThis research investigates the influence of single and hybrid mineral nanofillers on the morphological, thermal, and electrical properties of epoxy-based glass fiber composites. Nanocomposites were fabricated using hand lay-up technique, incorporating nano-calcium carbonate (CaCO₃) and nano-talc with particle size of 50 to 100 nm into an epoxy matrix with 5-ply E-glass/S-glass fiber. The study evaluates composites with 2-8 wt% of nano-CaCO₃, and hybrid systems containing nano-CaCO₃ (2-8 wt%) and nano-talc (1-4 wt%). Morphological analysis via Scanning Electron Microscopy (SEM) assessed nanofiller dispersion, while thermal properties were analyzed using Differential Scanning Calorimetry (DSC) for glass transition temperature (Tg). Electrical performance was evaluated through dielectric breakdown voltage (ASTM D149) and surface resistivity (ASTM D257). SEM analysis showed filler dispersion depended on concentration, with optimal distribution at 4-6 wt% before significant agglomeration at higher concentrations. DSC results revealed increased Tg with nanofillers, peaking for the composite with 6 wt% CaCO₃ and 3 wt% talc, indicating enhanced thermal stability. The dielectric breakdown voltage peaked at 17.6 kV for 2 wt% CaCO₃ and 1 wt% talc composite, while surface resistivity was highest for 4 wt% CaCO₃ and 2 wt% talc (73.74×1012Ω). All formulations maintained UL 94 V-1 flammability rating. The study concludes that the synergistic interaction between nano-CaCO₃ and nano-talc enables significant tailoring of thermal and electrical properties for advanced applications.
Magnesium oxide nanoparticles were deposited by laser pyrolysis process. Three types of lasers were employed CW CO2, Q-switched Nd-YAG (short pulses) and long pulses Nd-YAG lasers. The size and density of nanoparticles vary with laser energy, power, pulse duration and the scanning speed of the laser. In this method, MgO nanoparticles were deposited by a laser beam on a quartz substrate from aqueous solution of magnesium nitrate. AFM images reveal formation of small nanoparticle size of 24.5 nm with surface roughness 6.97nm by Q-switched Nd-YAG laser (10 ns) when the energy was 1J. While for CO2 laser, the smallest size was 18.8 nm at 0.4mm/s scanning speed with surface roughness 5.21nm at the same scanning speed. Moreover, long Nd-YAG pulses laser produces relatively larger average size of 37.5nm at 0.8ms pulse duration. The absorption spectra from UV-Visible spectroscopy were also conducted. The best absorption intensity was obtained at a wavelength ranging between 420-430 nm for both lasers. Finally, Thermal analysis using COMSOL Multiphysics software for the deposition process reveals that maximum temperature about 440Kfor Q-Switched Nd-YAG laser at 1J laser energy. While for RF CO2 laser, the maximum temperature obtained at 0.4mm/s scanning speed is 850K.This work provides a good knowledge for the deposition of nanoparticles using laser beams.