×
The submission system is temporarily under maintenance. Please send your manuscripts to
Go to Editorial ManagerStrengthening elastomers by the Nano-fillers, for example, Graphite subordinates, have high embellishments on their attributes. In the present work, Graphene Oxide (GO) nano-sheets have scattered in huge rubbers was Nitrile Butadiene Rubber (NBR). Enhancement the vulcanization procedure on (GO/NBR) nano-composite elastic was performed by arrangement blending strategy and rumination blending method. Scattering of GO into NBR was homogenous, where affirmed by Scanning Electron Microscopy (SEM) and X-beam Diffraction (XRD) test. Breaking down the useful gatherings by Fourier-Transformed Infrared Spectrophotometry (FTIR) has been explored as well. Diverse stacking wt% of GO inside NBR has clear impacts on the rigidity and flexibility conduct of the nano-composite. Impact of GO on the electrical conductivity and persuasive properties of GO/NBR nano-composite elastic portrayed too. The GO presence has upgraded the crosslinking trademark in GO/NBR nano-composite elastic and enhanced its properties.
Al2O3 is a major reinforcement in aluminum-based composites, which have been developing rapidly in recent years. The aim of this paper is to investigate the effect of alumina phases and amounts on the physical properties of fabricated Al-Al2O3 composite. Alpha micro and gamma nano of alumina with particle size of 30µm and 20 nm respectively reinforced aluminum matrix of 45 µm. The percentage of reinforcement material were in the range of (5, 10 and 15wt.%) fabricated by powder metallurgy technique. Specimens dimensions were a disc specimens with 11mm diameter and 5 mm thickness. The green density was achieved under compaction pressure of 500MPa, and then sintered under pressure less sintering at 500ºC in a vacuumed tube furnace for two hours Physical properties of the composite samples have been studied such as relative density, sintered density, porosity, microstructure characteristics, particles distribution, agglomeration, grain sizes and granularity accumulation distribution. It has been noticed that at the micro alumina phase, its relative densities are decreased when there is an increase in amount of micro alumina addition, on the contrary in case of nano composites, where the relative density are increasing along with the increase in nano alumina addition. At micro and nano composites, the produced relative densities are less than the pure aluminum relative density. Agglomeration are increasing with the increase in amount of reinforcement, while its more obvious with nano composite. Grain size reduced with the increase in amount of alumina in micro and nano composites, while, the obtained average grain size diameter is less in nano composite than in micro composites. It is obvious from the results that the variation in physical properties and microstructure of Al-Al2O3 composite are depends on both of alumina phases (size) and percentages. At 15wt.% of nano alumina higher relative density and lower porosity will be obtained.
This research is devoted to study the influence of different weight percent concerning to the additions of Ti and Cu on mechanical and tribological properties of AA6061. The composite materials consist of different weight percentage of Ti (0.2, 0.4, and 0.6) wt% and constant weight percentage of Cu (0.2) wt% which were fabricated by liquid metallurgy route technique. Microstructural characterization and phases have been examined by using SEM (scanning electron microscopic).SEM examination showed uniform distribution of nano Ti and Cu in AA6061. The consequences of mechanical tests demonstrated clear enhancement in mechanical properties, such as ultimate tensile strength, yield strength, young modulus, ductility% and hardness at additive percentage of 0.4% Ti+0.2%Cu nano particles incorporated into molten AA6061. Percentage of enhancement ultimate tensile strength is about 73.3%, yield strength about 82.7%, young modulus is about 21.2%, the Vickers hardness about 42.6% and the decreasing in ductility was about 25.2% compared with the metal matrix (AA6061). The wear rate test was performed by using pin on disc rig for both hybrid nano composite and base metal (AA6061) under various loads (10,15and 20) N with sliding speed (1.282) m/sec at a (10) min’s time. The results showed a decrease in wear rate at 0.4%Ti+0.2%Cu compared with the base metal (AA6061). Improvement percentage of wear rate is about 105% at 20 N load.