Go to Editorial ManagerFriction stir spot welding (FSSW) is a modern solid-state joining process able to weld similar and dissimilar overlap joints in different classes of materials and is widely being considered for automotive industry. In this work, the mechanical behavior ) i.e. tensile shear tests, Microhardness(, and microstructure of friction stir spot welded joints were studied for AA6061-T6 aluminum alloy sheets with thickness of 1.6 mm. Series of FSSW experiments were conducted using vertical CNC milling machine type "C-tek". FSSW is carried out at different pin profiles (cylindrical, taper, and triangular) and tool rotational typically speeds, i.e. 800, 1000, 1200 and 1400 rpm. Based on the welding experiments conducted in this study, the results show that sheets welded by triangular pin tool have highest tensile shear load, of 3.2 kN, followed by welds with cylindrical pin, while welds made using taper pin has the tensile shear load 2.1 kN at optimum speed of 1200 rpm. Also the pin shape and rotational speed had an obvious effect on microstructural parameters i.e. hook height and bond width.
This paper presents a comparison of using different techniques for stir spot welding of Aluminum 2024-T3, which are refill friction stir spot welding (RFSSW), edited (RFSSW-pin) and conventional friction stir spot welding (FSSW), depending on the obtained tensile shear strength property. Specimens were prepared from AA2024-T3 sheet for chemical analysis and mechanical tests. Workpieces were stir spot welded utilizing the above mentioned techniques at four rotational speeds (2000, 2500, 3000 and 4000 rpm) using tool pin diameters (5 and 7 mm) for conducting the tensile shear tests. The microhardness along the cross section of the welded specimens was conducted at the best conditions as well as the microstructure examination. The comparison results revealed that at the rotational speeds (2000 and 4000 rpm) in both cases of tool pin (5 and 7 mm), the ultimate tensile shear force was slightly higher than that for other speeds. However, the ultimate tensile shear force was found higher at 3000 rpm speed with a tool pin 7 mm. The microhardness results manifested a W-shape at the best conditions. Finally, the microstructure examination depicted the morphology of the main zones of the weld joint.