The submission system is temporarily under maintenance. Please send your manuscripts to
Go to Editorial ManagerMost of building rubbles or wastes contain some damaged materials such as cement, brick, steel, ceramic, plastic and other substances. Among these materials, ceramic and brick when using both of them as a partial replacement by the weight of conventional coarse aggregate in mixture concrete with presence of variety ratios ( 10% to 30%) for sawdust as replacement of fine aggregate, the resulting concrete properties will affected. So, this paper was based on the study some properties of concrete that produced of 50% replacement for those rubbles plus to presence 10%, 20% and 30% sawdust for both of them. The results revealed that present of sawdust with each of type of those rubbles provides database which are potential to be used in the production of lighter and economical new concrete material. Furthermore, the higher ratios of sawdust (more than 10 %) lead to obvious affected on the strength as well as other properties. While, those negative effects will perceptible improved when added 10% sawdust in ceramic aggregate concrete compared to brick aggregate concrete.
In the present work, the agricultural wastes which are wheat bran and raw okra waste used as adsorbent material for adsorption of cadmium and copper ions from wastewater .The effect of adsorption variable which include initial pH of solution , agitation speed, agitation time, initial concentration of cadmium and copper ions, and amount of adsorbent material were investigated in a batch process in order to obtain the maximum ions removal from wastewater .The results obtained from experimental investigation show that the percentage removal of metal ions increases with increasing pH and agitation speed until a maximize value after that it decreased with increasing pH and agitation speed. Also increases with increasing amount of adsorbent material and agitation time until a maximize value then reach a constant value approximately , and decreasing with increasing metal ions concentration .The maximum removal percent of cadmium and copper ions were 85.8% and 52.7 % respectively which obtained at pH equal 5.0, agitation speed 150 revolution per minute, agitation time 105 minute , metal ion concentration 40mg /L ,and adsorbent amount 1.5gm when using wheat bran as adsorbent material ,while obtained the maximum removal percent of cadmium and copper ions were 81.7% and 47.8 % which obtained at pH equal 6.0, and pH equal 5.0 respectively , agitation speed 150 revolution per minute, agitation time 90 minute ,metal ion concentration 40 mg /L ,and adsorbent amount 1.5gm when using okra waste as adsorbent material. From above result the wheat bran and okra waste was a best adsorbent material for removal cadmium and copper ions from wastewater but wheat bran slightly more effective than okra waste._x000D_
This paper present glass waste material reusing in concrete as partial replacement of cement. Some hardened properties like compressive and flexural strengths, modulus of elasticity and % absorption was made. The effect of glass powder on these properties was examined compared to reference specimens without glass powder. Five percentage was tested: 0%(reference), 10%, 15%, 20% and 25%. From tests results one can conclude that replacing cement partially by glass powder enhanced strengths of concrete (compression and flexural) up to 20% replacing level Using glass powder as partial replacement of cement improved strengths and modulus of elasticity of concrete. The %absorption decrease with increasing of glass powder content. The results show that utilization of waste glass as powder in concrete can reduce amount of cement which save cost besides its environmental benefits.