Go to Editorial ManagerExperiments were conducted to study the effect of quenching medium carbon steel in water-based MWCNTs nanofluids at 0.05 % wt. concentration quenchant, a large cylindrical sample with 46 mm diameter and 40 mm length made from medium carbon steel used with three K-type thermocouples with a diameter of 1.5 mm inserted in three locations for sample (center of the sample, mid-point between center and surface and 1 mm from the surface). A time-temperature reading data system was used to read temperature history during cooling stage.The same experiments were simulated using ANSYS Workbench with Thermal Transient Version 19, the cooling curves at three locations for the cylindrical steel sample calculated during quenching in MWCNTs nanofluids. Quench factor analysis was used to predict the hardness results from the calculated and measured cooling curves, and these results compared with the hardness test results conducted in the significant sample from the center to the surface. The results show excellent compatibility when compared between the hardness results from cooling curves, and it also shows a good agreement with the results of the hardness test, especially at the sample surface.
High-performance polymer nanocomposites utilizing different-sized nanofillers had a lot of interest recently. Due to their distinct structural, and thermal characteristics. Multi-wall carbon nanotubes (MWCNT) and nanoclay (NC) have the most interest among the numerous types of reinforcing as filler elements for a polymer. The formation of hybrid from MWCNT and NC at various loadings (0.5%, 1%, and 2wt%) on the characteristics of epoxy polymer have been assessed in this work. The specimens have been created using solution blending procedures with the addition of solvent ethanol at a ratio of 1:1 for dispersed nanofillers, and then they have been re-mixed with epoxy. Tests like X-Ray diffraction (XRD), and thermal conductivity were used to identify properties of epoxy. According to the test results, the thermal conductivity rise as the filler content rises at 1wt%, then start to decrease after 1wt%. The sample with the hybrid filler loading of 1 wt% produced the best performance. Since hybrid epoxy exhibits the best result of the thermal conductivity 135% over MWNT and NC nanocomposites of 1 wt.% reached 0.3568 W/m.K in the increased thermal conductivity property. By examining the EP nanocomposites XRD pattern. The hybrid of epoxy nanocomposites exhibits all of the NC and MWCNT characteristic peaks. Since interactions between the filler and the epoxy cause a shift in the peak location of 1wt%. Due to the homogeneity of the nanofillers entire epoxy matrix, there may be changes in the intensity or location of the peaks at 1% for 2θ= 20.13°, which corresponds to an interlayer distance of d=0.461nm.