Go to Editorial ManagerLiquid nitrate is an important method used to improve mechanical properties. One of these properties is resistance to fatigue. The aim of this study was to improve the fatigue resistance of the stainless steel 316L. The rotational bending method was used with constant and variable stresses at different times of (1, 3, 5) hours and at (530, 630) C0. These tests were performed before and after nitration._x000D_ The results showed that the depth of the nitride layer was (0.21, 0.33, 0.45) mm, increasing with time nitriding when the temperature was 530 C0. While the depth of this layer at a temperature of 630 C0 (0.26, 0.39,0.5) mm with increasing time. As a result of these processes, a layer of solid chromium nitrides and other phases of iron nitride were formed on the outer surface. These layers helped to inhibit the growth of the cracks and their progress in addition to the generation of pressure stresses on the surface leading to obstructing the progress of the cracks._x000D_ This study showed that the fatigue resistance was directly proportional to the increase in nitrate time due to the increased depth of the hardened layer, but this resistance decreased when the temperature was 630 C0 due to the formation of brittle phase with low resistance.
Desired mechanical properties like microstructure, micro hardness and wear resistance are the key parameters for which low carbon steel (AISI 1006) are widely selected. Surface heat treatment applied to improve these properties; traditionally surface heat treatments like induction hardening, in recent time’s laser surface hardening. In this work, thermochemical treatment (liquid nitriding) by using mixture from 61% NaCN, 15% K2CO3 and 24% KCL and followed by Nd:YAG laser surface treatment was done . The laser parameter were energy (0.89, 2, 4 and 9) J, spot diameter (0.790 ,0.33, 0.283 and 0.224) mm, pulses duration (1, 2.33, 4.47 and 9.87) ms with fix wavelength 1604nm. Laser surface treatment cycle was melting the layer surface, holding and rapid cooling in air medium. Optical microscopy (OM) and scanning electron microscope (SEM) has been used to study the microstructures and cross-sectional of molted and heat affected zones respectively. The wear test was done to measure the wear rate by using pin -on-disk principles were satisfied. The result shown that increasing in laser energy effects to increase in the area of melted and heat affected zones of nitriding steel. Also increasing in laser energy led to increase micro hardness about 61%, while wear rate decrease about 40 % and increased depth of molted zone.