The submission system is temporarily under maintenance. Please send your manuscripts to
Go to Editorial ManagerIn this work, waste glass powder from broken windows and plastic fibers from waste polyethylene terephthalate bottles are utilized to produce an economical self-compact concrete. Fresh properties (slump flow diameter, slump Flow T50, V. Funnel, L–Box), mechanical properties (Compressive strength and Flexural strength) and impact resistance of self-compact concrete are investigated. 15% waste glass powder as a partial replacement of cement with five percentages of polyethylene terephthalate plastic waste were adopted: 0% (reference), 0.5%, 0.75%, 1%, 1.25% and 1.5% by volume. It seems that the flow ability of self-compact concrete decreases with the increasing of the amount of plastic fibers. The compressive strength was increased slightly with plastic fiber content up to (0.75%), about 4.6% For more than (0.75%) plastic fiber. The compressive strength began to decrease about 15.2%. The results showed an improvement in flexural strength and an impact on the resistance in all tested specimens’ content of the plastic fibers, especially at (1.5%) fibers.
In this research, binary blends have been prepared from epoxy resin (EP) and different weight percentages of polysulfide rubber (PSR) (0%, 2.5%, 5%, 7.5 and 10%), and then compression, impact, and hardness tests were evaluated. The experimental results showed that the addition of polysulfide rubber in the epoxy resin decreased the compressive strength, Young's modulus, and hardness, while increased the impact resistance. It was found that the weight percentage 5% of polysulfide was the best percentage, which gives the best mechanical properties for the blend matrix. The advantage of this blend matrix is that, it mediates between the brittle properties of epoxy and the flexible properties of a blend matrix with the highest percentage of PSR. Short fibers (Carbon & Glass) with different volume percentage (2.5%, 5%, 7.5%, and 10%), were used to reinforce the best blend matrix obtained separately and randomly, and then the same mechanical tests conducted on these composites. The experimental results showed that the addition of fibers increased the compressive strength, Young's modulus, impact resistance and hardness. It was also observed that the composites materials reinforced with carbon fibers have significantly higher mechanical properties values than the composites materials reinforced with glass fibers.
The mechanical behavior of multilayer FRCMs was tested, and the effects of fibers, types of fiber, and laminates on the tensile, flexural, and impact properties were discussed. The vacuum bagging method is a composite manufacturing process that uses atmospheric pressure to consolidate laminate layers, remove excess resin, and get rid of air bubbles. This makes high-quality, void-free composites. Four composite systems were made using this method: natural fiber composites reinforced with sheep wool and goat hair fibers, and synthetic fiber composites reinforced with carbon and glass fibers, all with an epoxy resin (LR620) and hardener (LH620) system. All composite assemblies have been systematically characterized at different layer configurations (3-6 layers considered) for the best structural response. The tensile, flexural, and impact properties were tested by following the corresponding ASTM (D638, D790, D6110) standards, respectively. The tensile and flexural results of the carbon fiber composite (GCT, GCB series) showed excellent mechanical performance (maximum tensile strength of 283 MPa for GCT4 and flexural strength of 164 MPa for GCB5) with high load-carrying capacity, but the failure was brittle. Goat hair composites exhibited excellent impact resistance (GHI4: 1.255 J) and moderate tensile strength (36 MPa), which indicated superior energy absorption capacity. The glass fiber composites showed a good balance of mechanical properties with increased ductility, where the tensile strength was 245 MPa, and a large deflection capacity was reached (14.683 mm). The study demonstrates that 4-layer setups usually result in the highest tensile properties, while 5–6-layer setups improve the flexural strength. These results add to the knowledge of optimization of multilayer composite design, and they are very useful for materials selection in aerospace, automotive, and structural applications.
Reinforcement process of epoxy has been widely used to improvement of mechanical properties. Therefore, this work is concerned with the reinforcement of epoxy by adding natural materials (Pomegranate peel and Licorice particles) at epoxy. Different percentages of particles (5, 10, 15 and 20%) were used. The mechanical testing were included tensile, bending, hardness and impact tests. Hardness of epoxy was increased at increasing of Pomegranate peel (PP) and Licorice (L) percentages. Impact resistance of epoxy with Pomegranate peel (PP) has reached the highest at (10%), while with Licorice (L) has reached the highest at (5%). The results of tensile strength represent that increases of tensile strength at all percentages of (L), while (PP) showed that decreases at (5%) and increases at others percentage. Bending strength of epoxy has increased as increasing of (PP) at all percentage that used, but it has increased at (5, 10 and 20%) of (L), while it has dropped at (15%).