The submission system is temporarily under maintenance. Please send your manuscripts to
Go to Editorial ManagerThe main objective of the present paper is to investigate the effect of fineness moduli (FM) of fine aggregate on fresh properties (flow ability. Passing ability and segregation resistance), and hardened properties (compressive strength, split tensile strength, flexural strength and ultrasonic pulse velocity UPV) of self-compacting concrete (SCC). Four values of FM 2.3, 2.5, 2.7 and 3.1 were used, according to acceptance range of ASTM C33-03 for FM for fine aggregate, which recommended range for FM is 2.3 to 3.1._x000D_ Four series of mixes were casting , each series consist of two mixes represent normal strength and high strength SCC, each series of mixes made from fine aggregate have the same FM. Flow ability, passing ability.and segregation resistance of fresh SCC, both with normal and high strength decreases with increasing the fineness moduli. High strength SCC more effected than normal strength concrete due to increase the volume of particles. _x000D_ Great enhancement in compressive strength split tensile strength and flexural strength in both normal and high strength SCC when the FM is 2.5. Increase FM to 2.7 and 3.1 not lead to increase in strengths. The UPV values of normal and high strength SCC mixes have a good general condition. SCC mixes with FM 2.5 possess excellent general conditions.
The purpose of this research is to investigate how the fiber orientation and loading axis of a composite material affect its behavior. Consideration was given to two different fiber-to-matrix ratios in order to improve the mechanical properties. Hand lay-up samples were produced in accordance with ASTM D790 for flexural testing. On UTM, tensile and flexural tests were performed on the sample. The effect of fiber orientation modifies the composites' mechanical properties. As the fiber orientation increased, the tensile strength of the composite would reduce. This carbon/epoxy composite test demonstrates better strength than those conducted at (30, 5, 60, and 90 degrees). For flexural tests, a three-point bend at 30 degrees demonstrates excellent strength. Utilizing the three-point bend method, the flexural strength and flexural modulus have been determined. The tensile strength, young's modulus, elongation percentage, maximum load to break the composite, peak load, and flexural strength of single- and double-layered carbon fibers were compared and examined. As the number of layers increased, the adhesion between layers of epoxy and fiber carbon, and glass fiber weakened, causing a decrease in almost all mechanical properties. The fabricated 2024-T3 and epoxy glass fiber had higher fatigue strength than aramid reinforced and lower density than steel alloy utilized in aircraft manufacture.
In this work, waste glass powder from broken windows and plastic fibers from waste polyethylene terephthalate bottles are utilized to produce an economical self-compact concrete. Fresh properties (slump flow diameter, slump Flow T50, V. Funnel, L–Box), mechanical properties (Compressive strength and Flexural strength) and impact resistance of self-compact concrete are investigated. 15% waste glass powder as a partial replacement of cement with five percentages of polyethylene terephthalate plastic waste were adopted: 0% (reference), 0.5%, 0.75%, 1%, 1.25% and 1.5% by volume. It seems that the flow ability of self-compact concrete decreases with the increasing of the amount of plastic fibers. The compressive strength was increased slightly with plastic fiber content up to (0.75%), about 4.6% For more than (0.75%) plastic fiber. The compressive strength began to decrease about 15.2%. The results showed an improvement in flexural strength and an impact on the resistance in all tested specimens’ content of the plastic fibers, especially at (1.5%) fibers.
In this work chopped carbon fibers are used to improve tensile strength of Porcelanite lightweight aggregate concrete. Silica fume was added in order to improve the mixes compressive strength. Silica fume increase water demand and using fibers reduce workability, to improve workability and decrease water demand high rang super plasticizers are used. The results showed that compressive strength, splitting tensile strength, modulus of elasticity of carbon fibers Porcelanite lightweight aggregate concrete increase with increasing of carbon fiber up to 2% compared to reference Porcelanite lightweight aggregate concrete without fibers. The percentages of increasing were 14.40%, 68.00%, and 10.66% for compressive strength, splitting tensile strength, and modulus of elasticity, respectively. Flexural Strength continues in increase with increase of fibers. The dry unite weight of mixes with chopped fiber decrease with increase of fiber percentage. Besides the chopped carbon improved the ductility of Porcelanite lightweight aggregate concrete and that clear from stress-strain relationship.
This work covers mixing of unsaturated polyester (un- polyester) with starch powders as polymer blends and study the effects of irradiation by UV-acceleration on mechanical properties of its. The unsaturated polyester was mixing by starch powders at particle size less than (45 µm) at selected weight fraction of (0, 0.5, 1, 1.5, 2, 2.5 and 3%). These properties involve ultimate tensile strength, modulus of elasticity, elongation percentage, flexural modulus, flexural strength, fracture toughness, impact strength and hardness. The results illustrate decrease in the ultimate tensile strength at and elongation percentage, while increasing modulus of elasticity, with increasing the weight ratio of starch powder to 3 % weight fraction, whereas the maximum value of hardness and flexural, impact properties happened at 1 % weight fraction for types of polymer blends.
Glass is an inert material which could be used and recycled many times. Several tons of waste glass (WG) are generated annually worldwide due to the rapid growth of the population and improvement in the standard of living. In this study, the WG was used and supplied with three different particle sizes; 600?m, 2.36 mm and 4.75mm and partially weight replaced of fine aggregate at ratios 10%, 20% and 30%. The effectiveness of that changes on compressive strength and modulus of rupture at ages 28 and 90 days for concrete specimens produced were studied. The results showed that compressive and modulus of rupture at all ages increased along with addition of WG as glass powder (GP). Moreover, the specimens containing 30% of GP replaced has the best results, also it is found at this percentage of GP, more beneficial and capable to increased compressive and flexural strength up to 18.64% and 5.87 % respectively at 28-day compared to reference specimen. Besides, the test results revealed that at a replacement level 10% of 2.36mm fine glass (FG) has slightly improved the strength characteristics. While, the results demonstrated decreasing in that properties for the concrete specimens contained on coarse glass (CG) up to 4.75mm. The maximum negative effect on compressive strength and modulus of rupture recorded at the ratio 30% of CG where was the reduction in compressive strength 28.52% opposite 22.12% for modulus of rupture at age of 28-day. From that results, it can be concluded that the effect of FG was little compared to GP.
Normal concrete is weak against tensile strength, has low ductility and also insignificant resistance to cracking. The addition of diverse types of fibers at specific proportions can enhance the mechanical properties as well as the durability. Discrete fiber, which is commonly used, have many disadvantages such as balling the fiber, random distribution, and limitation of the used Vf ratio. Based on this vision, a new technique was discovered, enhancing concrete by textile-fiber to avoid all the problems mentioned above. This paper presents all important consequence and conclusions obtained from previous studies on how to strengthen concrete with two-dimensional and three-dimensional textile-fibers, and focuses on the flexural behavior of concrete members. The results indicate that there was an improvement in flexural strength, deformation capacity, and toughness with different load conditions when using different types of textile-fiber. It was observed that the effect of textile-fibers would increase when this fiber was coated by epoxy. In TRC system, there is a significant impact on the number of textile-fiber layers used.
This paper present glass waste material reusing in concrete as partial replacement of cement. Some hardened properties like compressive and flexural strengths, modulus of elasticity and % absorption was made. The effect of glass powder on these properties was examined compared to reference specimens without glass powder. Five percentage was tested: 0%(reference), 10%, 15%, 20% and 25%. From tests results one can conclude that replacing cement partially by glass powder enhanced strengths of concrete (compression and flexural) up to 20% replacing level Using glass powder as partial replacement of cement improved strengths and modulus of elasticity of concrete. The %absorption decrease with increasing of glass powder content. The results show that utilization of waste glass as powder in concrete can reduce amount of cement which save cost besides its environmental benefits.
The purpose of this study is to reduce weight and improve the mechanical properties of aircraft wing using Hybrid materials known as fiber metal laminates (FMLs). In this study, seven layers were used to produce the FMLs that consist of aluminum alloy2024-T3 reinforced by carbon and glass fibers bonded with blend of epoxy-resole. The Carbon Glass Reinforced Aluminum Laminates (CAGRALLs) was used as FMLs. The results showed that The CAGRALLs gave good mechanical properties because of increasing in tensile strength, elongation at fracture and impact toughness except flexural strength by comparing with other FMLs using commercial epoxy. The increasing in layers led to weaken adhesion force between layers of FMLs caused decreasing almost mechanical properties. The FMLs has good mechanical properties by using carbon and glass fibers by comparing with carbon and jute fibers. The CAGRALLs have higher numbers of cycles at failure under cyclic loadings than Aramid Reinforced Aluminum Laminates (ARALLs). The CAGRALLs have lower density by comparing with aluminum alloy 2024-T3 that used in manufacturing of aircraft wing.
Structural elements. This means the structural behavior can be quantified by considering the behavior of each structural element in each load path. Concrete is a material known for its great strength. Regardless, there are a few weaknesses, which must be taken in consideration in the design of concrete structural elements. Basically, concrete is made of three main ingredients: Portland cement, water, and aggregates (sand and stone).In order to improve tensile strength and ductility (capacity to stretch and deform prior to failure) in concrete, so this paper discus some types of concrete and record the effect on beams. Reactive powder concrete (RPC) is an actual concrete mixture, it is a special type of concrete because mix concrete (coarse and fine aggregate ) replaced by fine sand size (150-400)µm. In the experimental comparison the mechanical properties( compressive , splitting tensile and flexural )strength of plain RPC and high and normal strength concrete. Each set consisted of (4) cubes of (100×100×100_mm, (8) cylinder of (150×300mm) and (4) prism of (100x100x500) mm and consisted of (4) beam of (1000×100×400)mm. The results shown that the maximum compressive strength is 107 MPa and the maximum splitting tensile 9 MPa of RPC comparison high and normal strength concrete. The result of the second part shown increased RPC reinforced concrete the firstcrack288 MPa and ultimate crack 380MPa comparison high and normal strength concrete and the mode of failure of RPC (flexural-shear).