The submission system is temporarily under maintenance. Please send your manuscripts to
Go to Editorial ManagerThe corrosion behavior of martensite phase in Cu-Al-Be shape memory alloy with aging at 150 at time 2,4and 6 hour and quenching ice water with salt, water at room temperature and oil media study by open circuit potential, tafal polarization and cyclic polarization. The microstructure of martensite study by optical microscope and x-ray diffraction(XRD) and transformation temperature was determined by Di?erential Scanning Calorimeter (DSC).the result show aging martensite at 150 at 2 and 4 hour have high open circuit potential, low corrosion current density , high corrosion potential and pitting potential than martensite without aging.
The present work deals with direct diffusion bonding welding without interlayer of austenitic stainless steel type AISI 304L with Oxygen Free High Conductivity pure copper (OFHC) in vacuum atmosphere (1.5 *10-5 mbr.). The optimum bonding conditions are temperature of 650 ?C, duration time of 45 min. and the applied stress of 30 MPa, in order to secure a tight contact between the mating surfaces. The corrosion behavior of diffusion bonding joints in 3.5% Nacl is studied to evaluate the corrosion resistance of welding joints by using Potentiodynamic method. The observed microstructure of corroded specimen of optimum diffusion bonding joint shows that the corrosion current density has low value as compared with base materials used. During polarization, galvanic coupling is observed between two materials used. At passivity region, inverse polarity is occurred at 450mV. Therefore, passive stainless steel 304 L behaves as cathode respective to pure copper, the corrosion behavior of the diffusion bonding joint was mostly by copper side. The corrosion results indicate the presence of galvanic effect. The corrosion current density of copper, stainless steel 304L and bond joints condition were (3.66 µA/cm2, 1.62 µA/cm2 and 1.85µA/cm2) respectively. A SEM examination of corroded diffusion bonding joint indicates that the galvanic corrosion happened on copper side. The corrosion rate of bonding joint conditions was 0.85 mpy, which is less than 1%. This means that corrosion resistance of bond joint is more than excellent.
The electrodes material plays an important role in the amount of electricity produced in microbial fuel cells (MFCs). Metal electrodes used in MFCs are subject to biological and concentration cell corrosion which leads to a decrease in the cell efficiency. In the present work, the corrosion behavior of three selected electrode materials, namely, stainless steel, copper, and zinc under different operating conditions was investigated and discussed. In anode chamber, the microorganism (MO) used was Saccharomyces cerevisiae (yeast) with sodium acetate as a substrate forming the microbial corrosive solution. In the cathode chamber, the corrosive solution is aerated water. The effects of different operating parameters on the corrosion rate (CR) of these electrodes were studied such as: microorganism concentration, aeration of cathode chamber, and flow velocity in cathode chamber. The potential of the each electrode was measured to understand the corrosion behavior of electrodes and the produced current was also investigated. It was found that the corrosion rate of the electrodes in both anode and cathode chambers increases with increasing MO concentration in anode chamber and with increasing agitation speed in cathode chamber. The bio-corrosion is an important part of the corrosion occurring in microorganism chamber. The stainless steel exhibited the lowest corrosion rate for the whole investigated range of operating parameters followed by copper. The zinc electrode was found to be poor as an electrode in MFC as its corrosion rate was very high in all conditions investigated. In addition, this study showed that the air pumping in water chamber causes an appreciable increase in the corrosion rate in both chambers and an increase in the produced current.
In the present work the effect of heat treatment processes at different temperatures and in different quenching media on mechanical properties in addition to corrosion behavior in different pH solutions of aluminum alloy 6061 was achieved.The alloy was received as fabricated and the solution heat treatment processes was achieved at temperatures (490,530,570 °C), then quenching for every degree was done in two media (water, oil) to obtain on six samples. The artificial aging was done on every sample at temperature (160°C) for one hour.The microstructure was examined to show Mg2Si in every sample.The results of hardness test showed that the hardness of alloy increased with increasing heat treatment temperatures, and at the same temperature the quenched specimens in oil had higher hardness.On the other hand, the tension tests showed that the strength of alloy increased with increasing of heat treatment temperature, and at the same temperature the quenched specimens in water had higher hardness.The results of corrosions test showed that the heat treatment operations improved corrosion resistance, and the lower value was get upon treating at 530°C.