The submission system is temporarily under maintenance. Please send your manuscripts to
Go to Editorial ManagerThe purpose of this research is to investigate how the fiber orientation and loading axis of a composite material affect its behavior. Consideration was given to two different fiber-to-matrix ratios in order to improve the mechanical properties. Hand lay-up samples were produced in accordance with ASTM D790 for flexural testing. On UTM, tensile and flexural tests were performed on the sample. The effect of fiber orientation modifies the composites' mechanical properties. As the fiber orientation increased, the tensile strength of the composite would reduce. This carbon/epoxy composite test demonstrates better strength than those conducted at (30, 5, 60, and 90 degrees). For flexural tests, a three-point bend at 30 degrees demonstrates excellent strength. Utilizing the three-point bend method, the flexural strength and flexural modulus have been determined. The tensile strength, young's modulus, elongation percentage, maximum load to break the composite, peak load, and flexural strength of single- and double-layered carbon fibers were compared and examined. As the number of layers increased, the adhesion between layers of epoxy and fiber carbon, and glass fiber weakened, causing a decrease in almost all mechanical properties. The fabricated 2024-T3 and epoxy glass fiber had higher fatigue strength than aramid reinforced and lower density than steel alloy utilized in aircraft manufacture.
This work involved two major parts: the first one is the experimental part which included treatment of scoliosis deformity by manufacturing thoracolumbosacral orthosis, measuring the cobb angle of deformity, measuring the gait cycle data and walk path for both legs and suggesting a composite material to improve the mechanical properties of the orthosis and finally the interface pressure between trunk and orthosis is measured for twelve points covering of the total TLSO surface area by using f-socket devise. The second part of this study is the numerical simulation part during which the stresses are calculated using Ansys software for calculating stresses due to interface pressure loading boundary condition. The result shows no deference in gait cycle phases but the clear difference noted in walking path due to deviate center of mass, maximum pressure recorded left thoracic region with 900KPa due to correct spinal deformity while the minimum pressure recorded at right chest with l40KPa because of it is tissue region and Maximum value of stress was recorded at the left thoracic region with 2.81MPa due to Maximum interface pressure at this point.
In this study, the mechanical properties of an epoxy, unidirectional woven carbon and fiberglass composite were investigated experimentally. ASTM used for preparing the composite specimen. Different ranges of mixing ratios of woven carbon and fiberglass with epoxy are studied. Tensile, impact and bending test are carried out to investigate the mechanical properties for produced new composites. After testing the mechanical properties of the specimens, it is noted that adding of unidirectional woven carbon layers will leads to strengthens the samples. The mechanical properties of woven carbon composite are far superior to those of woven carbon composite with fiberglass.
In this work it had been focused on the possibility of replacement of steel spring in suspension system by fiber reinforced polymer composite that is responsible for light weight of spring which leads to reduces the weight of vehicle and improve fuel efficiency. This type of spring used in motor cycles, light weight vehicle. The design will be simulated by ANSYS workbench. Then, E-Glass fiber has been used to fabricate helical compression spring of 40% fiber volume fraction of glass. with polyester resin. The deflection of glass reinforced composite spring is more than steel spring but within permissible limit. weight of composite spring is reduced by 57% than of steel.
In this research, polymer polymethyl methacrylate PMMA composite with nano ceramic Zr and HAp material were used to manufacture one part of the implant system (femoral ball head of hip implant). Three set of hybrid materials were fabricated and tested for this study; the first mixtures which contains 100% (PMMA), the second mixtures which contains (90% (PMMA) + 8% (Zr) + 2% (HAp)), and the third mixtures which contains (80% (PMMA) + 18% (Zr) + 2% (HAp)) were investigated. The mechanical properties for these mixtures increased with the increasing of nano ceramic concentration (Zr and HAp) composite material in the polymer compared to pure polymer PMMA sample. However, an increase in the concentration of Zr from 8% to 18% content cause a considerable decrease of the hardness where a drop of homogeneity in Zr- matrix PMMA contact occurred, V Hardness value are (68 ,80 and 70) Kg.mm for three mixture respectively. The wear test was in agreement with results of the hardness test. The weight loss of the above samples of the wear test were (0.041, 0.035 and 0.037) respectively. According to mechanical properties, the best sample contains (90% (PMMA) + 8% (Zr) + 2% (HAp)). The Scanning electron microscopy resolute showed the particles forming semi-continuous network along grain boundaries polymer for second sample mixtures containing (90% (PMMA) + 8% (Zr) + 2% (HAp)), provides a low atomic packing and high energy. This will make the grain boundaries more reactive and strengthen mechanical performance. The Optical microscopy, Scanning electron microscopy and Xray spectroscopy analysis for In vitro test using SBF shows the growth of HAp layer with an increase in concentration of Ca and P elements formed on the surface of the second sample. This display of good results is a proof of the biocompatibility of the polymer sample.