The submission system is temporarily under maintenance. Please send your manuscripts to
Go to Editorial ManagerThe aim of this work is to determine the optimum parameters for deposition of chitosan and mixture of chitosan and hydroxyapatite (HA) layers using electrophoretic deposition. The layers were on 316L stainless steel substrate. Taguchi approach was utilized to select the optimum parameters for both layers. The parameters used for deposition chitosan are voltage, time and temperature while the parameters used for HA and chitosan are voltage, time, concentration and temperature. Zeta potential tests were employed to measure the solutions stability. Coating layers were characterized for thickness, porosity and nanoroughness using optical microscopy (OM) and atomic force microscopy (AFM). The results from Taguchi design of experiments demonstrated that the best conditions for deposition of chitosan and HA layers are 50 V, 5 min, 3 g HA/L and 30°C. The corresponding thickness, % porosity, nanoroughness and microroughness for optimum conditions were 22 µm, 3.53, 4.48 nm and 3.85 µm respectively.
The present work was designed on producing nanohydroxyapatite layers using electrophoretic deposition (EPD) on 316L stainless steel substrate. The EPD coatings were prepared by the deposition of hydroxyapatite (HA)-chitosan nanocomposites on different substrate roughness (polish surface, 220 grit SiC grind, and sand blast surfaces). Depositions were performed using the suspensions of HA nano particles (3 g/L) in the mixture of alcohol and distilled water (ethanol, 5 vol. %water and containing 0.5 g/L of chitosan dissolved in 1 vol.% acetic acid. Coatings were achieved on the cathode at constant voltage, time and temperature (90 V, 5 min and 40 °C respectively); the pH value was performed and fitted at 4. After deposition, the coated samples were dried at room temperature for 24 h. The surface topography of coatings was analyzed using atomic force microscopy (AFM). SEM was used to postulate both the surface and the cross section morphology of the coatings. The adhesion bonding between the deposited coatings and substrate were measured using tape tester to evaluate the adhesion bonding between the coating and substrate. The results showed the deposited coatings on sand blasted substrate has less porosity compared with the polish surface and 220 emery paper SiC grinding substrate respectively. The coating on the sand blasted substrate showed higher nanoroughness (122 nm), better adhesion bonding (removal area 15%) and higher thickness layer (12 µm) than that of the polish substrate and 220 emery paper SiC grinding substrate.
Biodegradable polymers are very useful polymers in biomedical applications. In this research, several hydrogels were fabricated by using two polymers, Polyvinyl alcohol (PVA) and Chitosan (Chs) by the solvent casting method in order to use them for skin applications. Several tests were carried out on these membranes such as Agar diffusion method to examine their antimicrobial activities, Fourier transform infrared microscopy (FTIR) test to study the differences in their chemical structures. Uniaxial tensile test was performed to examine the mechanical characteristics of these membranes. In addition, the wettability test was used to investigate the hydrophobicity or hydrophilicity of the surfaces. The results showed that all membranes are hydrophilic, of which the contact angles are less than 90°. The membrane manufactured from 75:25 Chs-PVA is more hydrophobic (contact angle is 74°) than other membranes made of 50:50 Chs-PVA and 25:75 Chs-PVA as the contact angles were 59° and 61°, respectively. The tensile test results indicate that the membrane fabricated of the PVA and the membrane that was fabricated by 75% Chs and 25% PVA has the highest tensile strength of 17.9 MPa, 16.2 MPa and Young^’ s Modulus of 181.2 MPa and 7.18 MPa, respectively. The highest strain at break was observed by the membrane of 25:75 Chs-PVA which equals to 24.67%. Chitosan membranes showed inhibition zones of about 2.99 cm and 2.75 cm in length, and 75:25 Chs-PVA membranes showed 5.1 and 5.91 cm in length for E.coli. To sum up, this copolymer is considered as promising hydrogel for skin applications such as wound dressing.