×
The submission system is temporarily under maintenance. Please send your manuscripts to
Go to Editorial ManagerOpen-graded-fraction-course (OGFC), is a hot asphalt mixture usually utilized as a private purpose wearing course, because of open graded asphalt mixture and aggregates skeleton (stone-on-stone) contact, it contain a relatively high air voids’ percentage, after compaction which are permeable to water. In this research one type of gradation was used (12.5 mm) NMAS, to preparing the OGFC asphalt mixtures, penetration grade 40/50, crushed aggregate, asphalt content prepared with 4 % and up to 6 % by weight of mixture with 0.5 % increments. Optimum asphalt content (OAC) was selected based on these criteria, air voids content, asphalt draindown, permeability, and abrasion resistance (aged and un-aged) condition. The mix performance had been investigated by indirect tensile strength and moisture susceptibility (sensitivity) measured according to the (AASHTO T283-14). Results illustrate that the increasing of asphalt binder content leads to a decrease of the air voids content, abrasion loss and permeability values, while draindown increase, conversely, the indirect tensile strength (ITS) had been significantly increased for both conditions and this is a gaod suggestion to resistance alongside moisture susceptibility. It can be decided that the increasing of asphalt binder percent in OGFC asphalt mixture, leads to an increase in the thickness of binder coating around the aggregates. On the other hand, the influence of modifier that prepared with 4% styrene-butadiene-styrene (SBS) on OGFC asphalt mixture tends to improve the mix properties and exhibit higher (TSR) as compared with original asphalt by (31, 27.7 and 24.4) % at asphalt percent (4.8, 5.3 and 5.8) %, respectively. The SBS improved the adhesion between aggregate and asphalt which leads to reduce stripping of HMA, horizontal deformation, and increased the tensile stiffness modulus value.
Open graded asphalt mixture is becoming more widespread where it is applied for various purposes, e.g. drainage of rainwater effectivity, traffic safety (high skid resistance), and controlling pollution noise. However, it has many other disadvantages, of which low stability, high stripping, and moisture sensitivity. The research aims to study the effect of styrene butadiene styrene SBS addition on the volumetric and mechanical properties of open graded mixture. In this research one type of aggregate with gradation (12.5 mm NMAS), asphalt of penetration grade (40/50), and cement as filler were used. Optimum asphalt content was selected based on the criteria of air voids content, asphalt drain down, permeability, and abrasion resistance (for aged and un-aged) samples. Other properties of open-graded mixtures, such as indirect tensile strength (ITS), moisture susceptibility, Marshall stability and flow were evaluated. The results show that addition of polymer (SBS) leads to an enhancement in the properties of the modified mixtures. There is an improvement in Marshall parameters. Also, a slight decreasing is noticed for permeability and air voids. For Cantabro abrasion loss (aging and un-aging condition), the abrasion resistance is increased, the drain down of asphalt is decreased from original mixture by addition of SBS. Finally, the moisture sensitivity is improved indicating that modified mixes becomes more resistant to water damage.