Go to Editorial ManagerMagnesium oxide nanoparticles were deposited by laser pyrolysis process. Three types of lasers were employed CW CO2, Q-switched Nd-YAG (short pulses) and long pulses Nd-YAG lasers. The size and density of nanoparticles vary with laser energy, power, pulse duration and the scanning speed of the laser. In this method, MgO nanoparticles were deposited by a laser beam on a quartz substrate from aqueous solution of magnesium nitrate. AFM images reveal formation of small nanoparticle size of 24.5 nm with surface roughness 6.97nm by Q-switched Nd-YAG laser (10 ns) when the energy was 1J. While for CO2 laser, the smallest size was 18.8 nm at 0.4mm/s scanning speed with surface roughness 5.21nm at the same scanning speed. Moreover, long Nd-YAG pulses laser produces relatively larger average size of 37.5nm at 0.8ms pulse duration. The absorption spectra from UV-Visible spectroscopy were also conducted. The best absorption intensity was obtained at a wavelength ranging between 420-430 nm for both lasers. Finally, Thermal analysis using COMSOL Multiphysics software for the deposition process reveals that maximum temperature about 440Kfor Q-Switched Nd-YAG laser at 1J laser energy. While for RF CO2 laser, the maximum temperature obtained at 0.4mm/s scanning speed is 850K.This work provides a good knowledge for the deposition of nanoparticles using laser beams.
Laser annealing represents a powerful method for tailoring the properties of silver nanofilms on quartz substrates, offering advantages in terms of precision, scalability, and functionalization. Continued research efforts are expected to deepen our understanding and broaden the applications of this promising technology in diverse fields. In this work, laser annealing of silver nanofilms deposited on quartz substrates was performed and investigated. RF CO2 laser of variable power in the range 1–20 W with beam quality of 1.1 was used to anneal silver nanofilms. AFM analysis emphasized that nanocrystal sizes of 60 nm were obtained for silver nanofilms. Furthermore, the optimum absorbance peak occurred at about 449 nm for smaller film thickness. Thermal simulation and analysis of the annealing process were also conducted using COMSOL Multiphysics software. It was observed that optimal temperature of 729 K was achieved when 10 W laser power and 2 mm/s scanning speed were used to anneal 20 nm silver film thickness. Design of expert analysis was also used to better understand the laser annealing process of silver nanofilms since convolution of several process parameters affect the process output.